FCFC TAIRIPRO® K1011 PP Resin

By /
FCFC TAIRIPRO® PP resin K1011

TAIRIPRO® K1011 PP Resin Injection Molding

TAIRIPRO K1011 Polypropylene Resin (K1011 Formosa) is a high-performance injection molding grade PP resin offering excellent stiffness and superior surface luster. It combines durability with aesthetic appeal while meeting USP Class VI safety standards.

  • Manufacturer: FCFC (Formosa Chemicals & Fibre Corporation）
  • Character: Good stiffness, Good luster
  • Application: General purpose, Foodcontainers, Electrical appliances, Housewares meets the requirements of USP Plastic Class VI
contact us
Please enable JavaScript in your browser to complete this form.
Click or drag files to this area to upload. You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Key technical data (ISO)

  • Melt Flow Index: 15 g/10 min (easy flow for fast, consistent molding)
  • Tensile Strength: 34 MPa (balances flexibility and strength)
  • Elongation at Break: >200% (resists cracking under stress)
  • Flame Rating: HB (UL 94 compliant for safe use in appliances)
  • Molding Shrinkage: 1.4–1.8% (predictable dimensions for precision parts)
  • Certifications: USP Class VI (food-safe), UL 746 electrical compliance.
  • Thermal & Electrical Performance: 65°C; PLC 2–4 ratings

Download

ISO Data SheetDownload
Safety Data Sheet SDSDownload
K1011 UL Product iQDownload
REACH SVHCDownload
Processing DataDownload

Exceptional Stiffness & Durability

With a flexural modulus of 1,421 MPa, K1011 Tairipro ensures rigid, warp-resistant parts—perfect for thin-walled food containers or appliance housings that require structural integrity under stress.

High Impact Resistance

Boasting 27 kJ/m² notched Izod impact strength, this PP K1011 resin withstands drops and impacts, making it ideal for durable housewares like storage bins or tool handles in demanding environments.

Heat-Resistant Performance

A heat deflection temperature of 110°C allows Tairipro PP resin to maintain shape in high-temperature applications, such as microwave-safe food containers or dishwasher-safe kitchenware.

TAIRIPRO K1011 PP resin

Application

  • Food Containers: Microwavable trays, reusable storage
  • Electrical Appliances: Housings, connectors
  • Housewares: Dishware, organizers
  • General Purpose: Automotive parts, industrial components
TAIRIPRO PP resin K1011 Application

Tairipro® K1011 Datasheet

Injection Molding Grade FCFC TAIRIPRO® K1011 Data Sheet
Product Description: Good stiffness, Good luster
PropertyUnitTest MethodTest ConditionModel K1011
Melt Flow Indexg/10 minISO 1133230℃ × 2.16kg15
IZOD Impact StrengthkJ/m²ISO 18023℃，1/8″，Notched27
IZOD Impact StrengthkJ/m²ISO 18023℃，4mm，Notched27
Specific Gravity–ISO 118323℃/23℃0.9
Tensile StrengthMpaISO 52723℃，50mm/min34
Tensile Elongation at break%ISO 52723℃，50mm/min>200
Flexural ModulusMpaISO 17823℃1421
Rockwell HardnessR-scaleISO 2039-223℃R-100
Heat Deflection Temperature℃ISO 75/AUnannealed，0.455Mpa 1/4″厚，120℃/h110
Molding Shrinkage%FCFC Method23℃1.4 ~ 1.8
CombustibilityUL-94File No. E162823HB 1.5 mm
All tests were run under laboratory conditions, ASTM, ISO testing procedures.
The data are intended as a general guide only.
Formosa Chemicals & Fibre Corp. Plastics Div.

Tairipro® K1011 UL Product iQ

TAIRIPRO® K1011 UL Product iQ
File Number: E162823Polypropylene (PP), pellets
FlammabilityValueTest Method
Flame Rating
1.5 mm, ALLHBUL 94
1.5 mm, ALLHB75IEC 60695-11-10, -20
ElectricalValueTest Method
Hot-wire Ignition (HWI) (1.5 mm)PLC 2UL 746
High Amp Arc Ignition (HAI) (1.5 mm)PLC 3UL 746
Comparative Tracking Index (CTI)PLC 0UL 746
High Voltage Arc Tracking Rate (HVTR)PLC 0UL 746
Arc ResistancePLC 4ASTM D495
ThermalValueTest Method
RTI ElecUL 746
1.5 mm65.0°C
3.0 mm65.0°C
RTI ImpUL 746
1.5 mm65.0°C
3.0 mm65.0°C
RTI StrUL 746
1.5 mm65.0°C
3.0 mm65.0°C

Related Tairipro® PP Plastics

1 2 3

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top