Chimei Polylac® PA-747F ABS

By /
Chimei POLYLAC PA-747F ABS Resin

Polylac® PA-747F Extrusion Grade High Rigidity Material


Polylac® PA-747F is a high-rigidity ABS resin engineered for extrusion and painting applications. Ideal for refrigerator plating, it combines durability, thermal stability, and excellent surface finish. With HB flammability certification, it meets stringent safety standards for appliances and industrial use.

  • Application: Refrigerator plating materialsPackaging: 25kg bag
  • Character: High rigidity profile extrusion materials. Best for Refrigerator plating, high-rigidity extrusion profiles, and painted industrial components.
contact us
Please enable JavaScript in your browser to complete this form.
Click or drag files to this area to upload. You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Key technical data (ISO)

  • Melt Flow Index: 3.5 ml/10 min (220°C)
  • Tensile Strength: 46 MPa (yield)
  • Impact Resistance: 30 KJ/m² (23°C), 20 KJ/m² (-30°C)
  • Thermal Stability: Vicat 106°C; Heat Distortion Temp up to 100°C (annealed).
  • Flammability: HB rating (1.5mm)
  • Mold Shrinkage: 0.4–0.7%

Download

ISO TDSDownload
ASTM TDSDownload
MSDSDownload
Process GuideDownload
UL Product iQDownload

Superior Rigidity for Extrusion

PA-747F’s tensile strength (46 MPa) and flexural modulus (1.9 GPa) ensure stable, warp-resistant profiles. Perfect for refrigerator door liners and industrial extrusions that demand precision.

Impact Resistance in Cold Environments

With 30 KJ/m² Izod impact strength (23°C) and 20 KJ/m² at -30°C, this ABS withstands drops and shocks, even in freezer components or outdoor settings.

Heat & Flame Safety Compliance

Vicat softening temperature of 106°C and HB flammability rating (UL 94) ensure reliability in high-heat zones like refrigerator compressors, while meeting global safety standards.

Chimei POLYLAC PA-747F ABS

Applications

  • Refrigerator Plating: Door liners, handles, and trim with flawless painted finishes.
  • Industrial Extrusions: High-strength profiles for machinery, automotive trims, and HVAC systems.
  • Safety-Critical Components: Compressor housings and electrical enclosures requiring flame resistance.
Chimei POLYLAC PA-747F application

Polylac® PA-747F Datasheet

Extrusion ABS POLYLAC®  PA-747F
Product Description: Refrigerator, Extrusion
PropertiesISO Test MethodTest ConditionUnitPA-747F
Melt Flow Index1133 220℃×10KGml/10 min3.5 
Mass Density1183 23 ℃g/cm31.05 
Tensile Strength527 50 mm/min, yieldMPa46 
50 mm/min, breakMPa33 
Tensile Elongation527 50 mm/min%25 
Flexural Strength178 2 mm/minMPa66 
Flexural Modulus2 mm/minGPa1.9 
Izod Impact Strength180/1A23℃, NotchedKJ/m230 
-30℃, NotchedKJ/m220 
Charpy Impact Strength179 23℃, NotchedKJ/m232 
-30℃, NotchedKJ/m221 
Vicat Softening Temp.306 50℃/hr;1KG℃106 
50℃/hr;5KG℃99 
Heat Distortion Temp.75/A1.8MPa, unannealed℃84 
1.8MPa, annealed℃100 
Coefficient of Linear Thermal Expansion11359 ––8.7 x 10-5
Flammability–UL-94–1.5mm HB
Mold Shrinkage294-4–%0.4~0.7
Symbol1043 ––>ABS<
March  12, 2025
Notes：These are typical properties only and are not to be construed as specifications. Users
should confirm results by their own test

Polylac® PA-747F UL Product iQ

POLYLAC® PA-747F | UL Product iQ
File Number: E56070Yellow Card™Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets
FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityANSI/UL 94
1.5 mm, Color: ALLHB
3.0 mm, Color: ALLHB
ISO/IEC FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityIEC 60695-11-10
1.5 mm, Color: ALLHB75
3.0 mm, Color: ALLHB40
ELECTRICAL PROPERTIESVALUETEST METHOD
Hot-wire Ignition (HWI)UL 746A
1.5 mmPLC 4
3.0 mmPLC 3
High Amp Arc Ignition (HAI)UL 746A
1.5 mmPLC 0
3.0 mmPLC 0
Comparative Tracking Index (CTI)PLC 1UL 746A
High Voltage Arc Tracking Rate (HVTR)PLC 0
High Voltage, Low Current Arc ResistancePLC 6
THERMAL PROPERTIESVALUETEST METHOD
Relative Thermal Index – Electrical StrengthUL 746B
1.5 mm60   °C
3.0 mm60   °C
Relative Thermal Index – Mechanical ImpactUL 746B
1.5 mm60   °C
3.0 mm60   °C
Relative Thermal Index – Mechanical StrengthUL 746B
1.5 mm60   °C
3.0 mm60   °C

Related Polylac® ABS Plastics

1 2 3

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top