Chimei Polylac® PA-747S A01 ABS

By /
Chimei POLYLAC PA-747S A01 ABS Resin

Polylac® PA-747S A01 Standard White Color Pre-colored


Polylac PA-747S A01 is a high-impact, pre-colored white ABS resin engineered for extrusion and injection molding. With superior strength, smooth flow, and thermal stability, it’s ideal for demanding industrial applications requiring durability and consistent aesthetics.

  • Character: High strength for extrusion, injection, standard white pre-colored
contact us
Drag & Drop Files, Choose Files to Upload You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Key technical data (ISO)

  • Melt Flow Index: 6 ml/10min (220°C/10KG)
  • Impact Strength: 35 KJ/m² (23°C, Notched)
  • Thermal Resistance: Vicat 106°C / HDT 96°C (1.8MPa)
  • Flammability Rating: UL94 HB (1.5mm)
  • Mold Shrinkage: 0.4–0.7%

Download

ISO TDSDownload
ASTM TDSDownload
MSDSDownload
Process GuideDownload
UL Product iQDownload

Exceptional Impact Resistance

The White ABS POLYLAC® PA-747S A01 delivers 35 KJ/m² Izod impact strength (23°C), ensuring parts like automotive trim or appliance panels resist cracking during assembly or daily use.

Effortless Processing

A Melt Flow Index of 6 ml/10min (220°C/10KG) allows seamless filling of complex molds, reducing cycle times for injection-molded components like housings or protective covers.

Reliable Thermal Performance

With a Vicat softening temperature of 106°C, this Chimei PA-747S A01 ABS maintains structural integrity in high-heat environments, such as near electronics or under UV coatings.

Chimei POLYLAC PA-747S A01 ABS

Applications

  • Sheet Extrusion: Durable panels for appliances, signage, or automotive interiors.
  • High-Impact Injection Parts: Protective equipment, tool housings, and consumer electronics.
  • Thermally Stable Components: Parts exposed to heat, such as lighting fixtures or HVAC ducts.
Chimei POLYLAC PA-747S A01 application

Polylac® PA-747S A01 Datasheet

White ABS POLYLAC®  PA-747S_A01
Product Description: High impact, Extrusion,white
PropertiesISO Test MethodTest ConditionUnitPA-747S_A01
Melt Flow Index1133 220℃×10KGml/10 min6 
Mass Density1183 23 ℃g/cm31.07 
Tensile Strength527 50 mm/min, yieldMPa40 
50 mm/min, breakMPa30 
Tensile Elongation527 50 mm/min%35 
Flexural Strength178 2 mm/minMPa60 
Flexural Modulus2 mm/minGPa2 
Izod Impact Strength180/1A23℃, NotchedKJ/m235 
-30℃, NotchedKJ/m2–
Charpy Impact Strength179 23℃, NotchedKJ/m235 
-30℃, NotchedKJ/m2–
Vicat Softening Temp.306 50℃/hr;1KG℃106 
50℃/hr;5KG℃101 
Heat Distortion Temp.75/A1.8MPa, unannealed℃–
1.8MPa, annealed℃96 
Coefficient of Linear Thermal Expansion11359 ––8.6 x 10-5
Flammability–UL-94–1.5mm HB
Mold Shrinkage294-4–%0.4~0.7
Symbol1043 ––>ABS<
March  12, 2025
Notes：These are typical properties only and are not to be construed as specifications. Users
should confirm results by their own test

Polylac® PA-747S A01 UL Product iQ

POLYLAC® PA-747S A01 | UL Product iQ
File Number: E56070Yellow Card™Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets
FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityANSI/UL 94
1.5 mm, Color: WTHB
3.0 mm, Color: WTHB
ISO/IEC FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityIEC 60695-11-10
1.5 mm, Color: WTHB75
3.0 mm, Color: WTHB40
ELECTRICAL PROPERTIESVALUETEST METHOD
Hot-wire Ignition (HWI)UL 746A
1.5 mmPLC 3
3.0 mmPLC 3
High Amp Arc Ignition (HAI)UL 746A
1.5 mmPLC 0
3.0 mmPLC 0
Comparative Tracking Index (CTI)PLC 1UL 746A
High Voltage Arc Tracking Rate (HVTR)PLC 0
High Voltage, Low Current Arc ResistancePLC 6
THERMAL PROPERTIESVALUETEST METHOD
Relative Thermal Index – Electrical StrengthUL 746B
1.5 mm60   °C
3.0 mm60   °C
Relative Thermal Index – Mechanical ImpactUL 746B
1.5 mm60   °C
3.0 mm60   °C
Relative Thermal Index – Mechanical StrengthUL 746B
1.5 mm60   °C
3.0 mm60   °C

Related Polylac® ABS Plastics

1 2

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top