Kibisan® PN-106 L150 General Purpose Grade SAN Resin
The KIBISAN PN-106 L150 is a high-transparency, chemical-resistant SAN resin engineered for durability and precision. Ideal for industrial applications like medical devices, food packaging, and automotive components, this General SAN KIBISAN® PN-106 L150 balances clarity, strength, and resistance to harsh environments.
- Application: General products requiring chemical resistance properties
- Character: High transparency, chemical resistance
Key technical data (ISO)
- Melt Flow Index: 32 ml/10 min
- Tensile Strength: 65 MPa
- Vicat Softening Temperature: 104°C (1KG)
- Flammability Rating: UL94 HB (1.5mm)
- Mold Shrinkage: 0.2–0.7%
Applications
- Medical Devices: Syringe barrels, IV connectors (resists sterilization chemicals).
- Food Packaging: Transparent containers, lids (safe for direct food contact).
- Automotive: Dashboard components, light covers (durable under heat and vibration).
- Consumer Goods: Cosmetic casings, household tools (scratch-resistant and visually appealing).
Kibisan® PN-106 L150 Datasheet
| General SAN KIBISAN® PN-106_L150 Product Description: High clarity | ||||
| Properties | ISO Test Method | Test Condition | Unit | PN-106_L150 |
| Melt Flow Index | 1133 | 220℃×10KG | ml/10 min | 32 |
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.06 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 65 |
| 50 mm/min, break | MPa | 65 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 3 |
| Flexural Strength | 178 | 2 mm/min | MPa | 89 |
| Flexural Modulus | 2 mm/min | GPa | 2.6 | |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 2 |
| -30℃, Notched | KJ/m2 | – | ||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 2 |
| -30℃, Notched | KJ/m2 | – | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 104 |
| 50℃/hr;5KG | ℃ | 101 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 88 |
| 1.8MPa, annealed | ℃ | 99 | ||
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 3.6~3.8*10-5 |
| Flammability | – | UL-94 | – | 1.5mm HB |
| Mold Shrinkage | 294-4 | – | % | 0.2~0.7 |
| Symbol | 1043 | – | – | >SAN< |
| March 11, 2024 Notes：These are typical properties only and are not to be construed as specifications. Users should confirm results by their own test | ||||
Kibisan® PN-106 L150 UL Product iQ
| KIBISAN® PN-106(+) | UL Product iQ | ||
| File Number: E56070 | Yellow Card™ | Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets |
| (+) – Indicate 0~0.5% acid scavengers. | ||
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.5 mm, Color: ALL | HB | |
| 3.0 mm, Color: ALL | HB | |
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.5 mm, Color: ALL | HB75 | |
| 3.0 mm, Color: ALL | HB40 | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | UL 746A | |
| 1.5 mm | PLC 3 | |
| 3.0 mm | PLC 3 | |
| High Amp Arc Ignition (HAI) | UL 746A | |
| 1.5 mm | PLC 0 | |
| 3.0 mm | PLC 0 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746A |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | |
| High Voltage, Low Current Arc Resistance | PLC 5 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |
Related Kibisan® SAN (aS) Plastics
Chimei Kibisan® PN-137H SAN
Chimei Kibisan® PN-127 L150FG
Chimei Kibisan® PN-127 L200
Chimei Kibisan® PN-127 L150
Chimei Kibisan® PN-117H L150FG
Chimei Kibisan® PN-117C
Chimei Kibisan® PN-117 L100
Chimei Kibisan® PN-106 L150
Chimei Kibisan® PN-127H SAN
Chimei Kibisan® PN-107 L125 SAN
Chimei Kibisan® PN-117 L200 SAN
Chimei Kibisan® PN-127 L100
Chimei Kibisan® PN-107 L125FG
Advanced Manufacturing