Chimei WONDERLITE® PC-616LS

Chimei WONDERLITE PC-616LS Flame Retardant Low Smoke Density

WONDERLITE® PC-616LS, a premium polycarbonate resin by Chimei, designed for industries that prioritize safety and performance. This non-brominated and non-chlorinated flame retardant material offers a low smoke density rating of 1.0 mm V0, making it an ideal choice for applications requiring enhanced fire safety without compromising on durability.

Application: Rail transportation application/Electrical appliances
Character: Non-brominated and non-chlorinated flame/1.0 mm V0, Low smoke density

PC Resin

Chimei WONDERLITE® PC Resin

Key technical data (ISO)

Density: 1.20 g/cm³
Tensile Strength: 65 MPa
Flexural Modulus: 2400 MPa
Izod Notched Impact Strength: 30 kJ/m²
Heat Deflection Temperature (HDT): 130°C at 1.8 MPa
Glass Transition Temperature (Tg): 147°C
Recommended Processing Temperature: 240-270°C
Drying Temperature: 80°C for 2-4 hours (prior to processing)
Fire Safety Standards: UL 94 V0, IEC 60695-11-10

Download

ISO TDS Download

MSDS Download

Process Guide Download

UL Product iQ Download

Exceptional Flame Resistance

WONDERLITE® PC-616LS is engineered with superior flame-retardant properties, ensuring maximum safety in critical applications. This feature is essential for industries like rail transportation and electrical appliances, where fire risks are a significant concern.

Low Smoke Density

With its low smoke density, PC-616LS minimizes the risk of smoke inhalation during a fire incident. This characteristic is crucial for environments such as public transport, where passenger safety is paramount, providing peace of mind to both manufacturers and end-users.

Versatile Application Compatibility

This polycarbonate resin is suitable for a wide range of applications, from rail components to electrical housings. Its adaptability means that procurement managers can streamline their sourcing processes, knowing that WONDERLITE® PC-616LS meets diverse industry requirements.

Application

Rail Transportation Application: Used in interior components and safety features, ensuring compliance with stringent safety regulations.
Electrical Appliances: Perfect for housings and parts that require flame resistance, enhancing safety and reliability in everyday use.

WONDERLITE® PC-616LS Datasheet

Flame Retardant WONDERLITE® PC-616LS Product Description: 1.0mm V-0, Low smoke density,Opaque
Properties	ISO Test Method	Test Condition	Unit	PC-616LS
Melt Flow Index	1133	300℃ × 1.2KG	ml/10 min	10
Spiral flow	CHIMEI	260℃,2mm, V:50%,P:50%	cm	–
Mass Density	1183	23 ℃	g/cm3	1.2
Tensile Strength	527	50 mm/min, yield	MPa	60
Tensile Strength	527	50 mm/min, break	MPa	70
Tensile Elongation	527	50 mm/min	%	110
Flexural Strength	178	2 mm/min	MPa	90
Flexural Modulus	178	2 mm/min	GPa	2.3
Izod Impact Strength	180/1A	23℃, Notched	KJ/m2	60
Izod Impact Strength	180/1A	-30℃, Notched	KJ/m2	15
Charpy Impact Strength	179	23℃, Notched	KJ/m2	60
Charpy Impact Strength	179	-30℃, Notched	KJ/m2	15
Vicat Softening Temp.	306	50℃/hr;1KG	℃	150
Vicat Softening Temp.	306	50℃/hr;5KG	℃	145
Heat Distortion Temp.	75/A	1.8MPa, unannealed	℃	125
Heat Distortion Temp.	75/A	1.8MPa, annealed	℃	140
Dielectric Constant	IEC 60250	1MHz	—	3
Volume Resistivity	IEC 60093	—	Ohm X m	3.6E+14
Surface Resistivity	IEC 60093	—	Ohm	9.3E+14
Coefficient of Linear Thermal Expansion	11359	–	–	6.7*10-5
Flammability	–	UL-94	–	1.0mm V-0 2.0mm 5VB 3.0mm 5VA
Mold Shrinkage	294-4	–	%	0.4~0.6
Symbol	1043	–	–	>PC<
January 12, 2024 Notes：These are typical properties only and are not to be construed as specifications. Users should confirm results by their own test

WONDERLITE® PC-616LS UL Product iQ

WONDERLITE® PC-616LS(f1)(a) \| UL Product iQ
File Number: E56070	Yellow Card™	Polycarbonate (PC) “WONDERLITE”, furnished as pellets
(f1) – Suitable for outdoor use with respect to exposure to Ultraviolet Light, Water Exposure and Immersion in accordance with UL 746C.
(a) – Ball pressure temperature is in accordance with IEC 60695-10-2 Method B.
FLAMMABILITY PROPERTIES	VALUE	TEST METHOD
Flammability		ANSI/UL 94
1.5 mm, Color: ALL	V-0
2.0 mm, Color: ALL	V-0
2.5 mm, Color: ALL	V-0
3.0 mm, Color: ALL	V-0
ISO/IEC FLAMMABILITY PROPERTIES	VALUE	TEST METHOD
Flammability		IEC 60695-11-10
1.5 mm, Color: ALL	V-0
2.0 mm, Color: ALL	V-0
2.5 mm, Color: ALL	V-0
3.0 mm, Color: ALL	V-0
Glow Wire Ignition Temperature (GWIT)		IEC 60695-2-13
1.5 mm	875 °C
3.0 mm	875 °C
Glow Wire Flammability Index (GWFI)		IEC 60695-2-12
1.5 mm	960 °C
3.0 mm	960 °C
ELECTRICAL PROPERTIES	VALUE	TEST METHOD
Hot-wire Ignition (HWI)		UL 746A
1.5 mm	PLC 3
2.0 mm	PLC 2
2.5 mm	PLC 2
3.0 mm	PLC 0
High Amp Arc Ignition (HAI)		UL 746A
1.5 mm	PLC 1
2.0 mm	PLC 0
2.5 mm	PLC 0
3.0 mm	PLC 0
Comparative Tracking Index (CTI)	PLC 2	UL 746A
Dielectric Strength	31 kV/mm	ASTM D149
Volume Resistivity	1.0E+14 ohms·cm	ASTM D257/IEC 60093
THERMAL PROPERTIES	VALUE	TEST METHOD
Relative Thermal Index – Electrical Strength		UL 746B
1.5 mm	130 °C
2.0 mm	130 °C
2.5 mm	130 °C
3.0 mm	130 °C
Relative Thermal Index – Mechanical Impact		UL 746B
1.5 mm	120 °C
2.0 mm	120 °C
2.5 mm	120 °C
3.0 mm	120 °C
Relative Thermal Index – Mechanical Strength		UL 746B
1.5 mm	130 °C
2.0 mm	130 °C
2.5 mm	130 °C
3.0 mm	130 °C
Ball Pressure Temperature	135 °C
PHYSICAL PROPERTIES	VALUE	TEST METHOD
Dimensional Change	0.0 %	ASTM D1042/ISO 2796
UV Exposure & Water Immersion	f1	UL 746C

Chimei WONDERLITE® PC-616LS