SABIC® PC Resin PC0700

Sabic PC Resin PC0700 Compounding Grade

Sabic PC0700 is a heat-stabilized, low-flow polycarbonate. This base resin is engineered for custom compounding, offering a robust foundation for high-performance, durable applications.

Character: low flow (MFR = 7 at 300°C/1.2kg), heat stabilized

PC Resin

Sabic® PC Resin

Key technical data

Tensile Stress at Yield: 63 MPa
Flexural Modulus: 2300 MPa
Notched Izod Impact (23°C): 900 J/m (ASTM) / 70 kJ/m² (ISO)
Heat Deflection Temp (HDT) @ 1.82 MPa: 127 °C
Vicat Softening Temperature: 144 °C
Melt Flow Rate (300°C/1.2kg): 7 g/10 min
Specific Gravity: 1.20
Mold Shrinkage, Flow: 0.5 – 0.7 %
Recommended Melt Temperature: 290 – 320 °C
Light Transmission (2.54mm): 88 – 90%
Haze: <0.8% Volume Resistivity: >1.E+15 Ω·cm
Dielectric Strength: 27 kV/mm

Download

SABIC® PC Resin PC0700 Americas TDS Download

SABIC® PC Resin PC0700 Asia TDS Download

SABIC® PC Resin PC0700 Europe TDS Download

Application

Automotive Lenses

Features & Benefits

Exceptional Impact Resistance & Toughness

With its high notched Izod impact strength, this PC resin helps prevent cracks and breaks, even in demanding environments, ensuring product longevity and reducing failure rates.

High Heat Deflection Temperature

Its excellent heat resistance allows components to maintain structural integrity at elevated temperatures, ideal for applications exposed to heat or requiring sterilization.

Superior Optical Clarity & Transparency

This resin provides outstanding light transmission with low haze, making it perfect for clear lenses and covers that require both durability and brilliant visual performance.