Kibisan® PN-117H L150FG Low Residual Monomer Grade SAN
AS(SAN) KIBISAN® PN-117H L150FG is a low residual monomer SAN resin certified for food safety (EU 10/2011, GB4806). With high strength, chemical resistance, and heat stability, it’s engineered for demanding applications like kitchenware and consumer goods.
- Application: Coffee machines, water jars
- Character: Low monomer residue (EU 10/2011 Certification, GB4806), high strength, high chemical resistance
Key technical data (ISO)
- Melt Flow Index: 8 ml/10 min (220°C, 10kg)
- Tensile Strength: 74 MPa
- Heat Resistance: Vicat 108°C (1kg) / HDT 104°C (annealed)
- Flammability: UL94 HB (1.5mm)
- Mold Shrinkage: 0.2–0.7%
- Certifications: Compliant with EU 10/2011 and GB4806 for food-contact safety.
Applications
- Coffee Machines: Withstands high-temperature water and steam, while resisting coffee oils and cleaning chemicals.
- Water Jars: Safe for drinking water storage, durable against impacts, and compliant with global food-safety standards.
Kibisan® PN-117H L150FG Datasheet
| Low Residual Monomer SAN KIBISAN® PN-117H_L150FG Product Description: High strength Chemcial resistant | ||||
| Properties | ISO Test Method | Test Condition | Unit | PN- 117H_L150FG |
| Melt Flow Index | 1133 | 220℃×10KG | ml/10 min | 8 |
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.06 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 74 |
| 50 mm/min, break | MPa | 74 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 3 |
| Flexural Strength | 178 | 2 mm/min | MPa | 121 |
| Flexural Modulus | 2 mm/min | GPa | 3.6 | |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 3 |
| -30℃, Notched | KJ/m2 | |||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 3 |
| -30℃, Notched | KJ/m2 | – | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 108 |
| 50℃/hr;5KG | ℃ | 104 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 86 |
| 1.8MPa, annealed | ℃ | 104 | ||
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 3.6~3.8*10-5 |
| Flammability | – | UL-94 | – | 1.5mm HB |
| Mold Shrinkage | 294-4 | – | % | 0.2~0.7 |
| Symbol | 1043 | – | – | >SAN< |
| March 11, 2024 Notes：These are typical properties only and are not to be construed as specifications. Users should confirm results by their own test | ||||
Kibisan® PN-117H L150FG UL Product iQ
| KIBISAN® PN-117H L150 FG | UL Product iQ | ||
| File Number: E56070 | Yellow Card™ | Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets |
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.5 mm, Color: ALL | HB | |
| 3.0 mm, Color: ALL | HB | |
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.5 mm, Color: ALL | HB75 | |
| 3.0 mm, Color: ALL | HB40 | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | UL 746A | |
| 1.5 mm | PLC 4 | |
| 3.0 mm | PLC 4 | |
| High Amp Arc Ignition (HAI) | UL 746A | |
| 1.5 mm | PLC 2 | |
| 3.0 mm | PLC 2 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746A |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | |
| High Voltage, Low Current Arc Resistance | PLC 5 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |
Related Kibisan® SAN (aS) Plastics
Chimei Kibisan® PN-137H SAN
Chimei Kibisan® PN-127 L150FG
Chimei Kibisan® PN-127 L200
Chimei Kibisan® PN-127 L150
Chimei Kibisan® PN-117H L150FG
Chimei Kibisan® PN-117C
Chimei Kibisan® PN-117 L100
Chimei Kibisan® PN-106 L150
Chimei Kibisan® PN-127H SAN
Chimei Kibisan® PN-107 L125 SAN
Chimei Kibisan® PN-117 L200 SAN
Chimei Kibisan® PN-127 L100
Chimei Kibisan® PN-107 L125FG
Advanced Manufacturing