Chimei Kibisan® PN-127 L100

By /
Chimei Kibisan PN-127 L100 SAN Resin

Kibisan® PN-127 L100 Injection Molding Heat Resistant

Kibisan PN-127 L100 SAN Resin is a tough, heat-resistant plastic ideal for industrial use. Its natural amber color hides flaws while giving products a clean look. It can withstands 105°C heat. Easy-to-mold (17 ml/10 min melt flow) and low-shrinkage (0.2–0.7%), it ensures precise, durable parts. Boasts 74MPa tensile strength and UL94 HB flammability for safety.

Basic Features:

  • Manufacturer: CHIMEI
  • Application: External pen tubing, transparent parts for electrical and electronic products, fan blades
  • Character: Natural amber color, heat resistant grade
contact us
Please enable JavaScript in your browser to complete this form.
Click or drag files to this area to upload. You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Heat-Resistant for Tough Jobs

It can withstand up to 105°C (Vicat softening), making it ideal for fan blades or electronics in hot environments. Stays rigid without warping.

Strong Yet Lightweight Build

Tensile strength of 74 MPa and flexural strength of 105 MPa handle stress, while 1.06 g/cm³ density keeps parts light and easy to use.

Easy to Mold Precisely

Melt flow of 17 ml/10 min ensures smooth shaping into complex designs. Low shrinkage (0.2–0.7%) reduces defects for crisp, accurate parts every time.

Kibisan PN-127 L100 SAN Resin

Download

Access essential product documentation including technical datasheets, safety information, environmental certifications, and processing guides. All documents are sourced directly from manufacturers and updated regularly for accuracy.

ISO TDSDownload
ASTM TDSDownload
MSDSDownload
UL Product iQDownload
RoHSDownload
REACH SVHCDownload
Process GuideDownload
Chimei Kibisan® PN-127 L100 Application

Kibisan® PN-127 L100 Datasheet

General SAN KIBISAN® PN-127 L100
Product Description: Injection molding
PropertiesISO Test MethodTest ConditionUnitPN-127_L100
Melt Flow Index1133220℃×10KGml/10 min17
Mass Density118323  ℃g/cm31.06
Tensile Strength52750 mm/min, yieldMPa74
50 mm/min, breakMPa74
Tensile Elongation52750 mm/min%3
Flexural Strength1782 mm/minMPa105
Flexural Modulus1782 mm/minGPa3.3
Izod Impact Strength180/1A23℃, NotchedKJ/m23
-30℃, NotchedKJ/m2–
Charpy Impact Strength17923℃, NotchedKJ/m22
-30℃, NotchedKJ/m2–
Vicat Softening Temp.30650℃/hr;1KG℃105
50℃/hr;5KG℃104
Heat Distortion Temp.75/A1.8MPa, unannealed℃90
1.8MPa, annealed℃101
Coefficient of Linear Thermal Expansion11359––3.6~3.8*10-5
Flammability–UL-94–1.5mm HB
Mold Shrinkage294-4–%0.2~0.7
Symbol1043––>SAN<
March 11, 2024

Kibisan® PN-127 L100 UL Product iQ

KIBISAN® PN-127 UL Product iQ
File Number: E56070Yellow Card™Styrene Acrylonitrile (SAN) “KIBISAN”, furnished as pellets
FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityANSI/UL 94
1.5 mm, Color: ALLHB
3.0 mm, Color: ALLHB
FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityANSI/UL 94
1.5 mm, Color: ALLHB
3.0 mm, Color: ALLHB
ISO/IEC FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityIEC 60695-11-10
1.5 mm, Color: ALLHB75
3.0 mm, Color: ALLHB40
ELECTRICAL PROPERTIESVALUETEST METHOD
Hot-wire Ignition (HWI)PLC 4UL 746A
(1.5 mm)
High Amp Arc Ignition (HAI)PLC 0UL 746A
(1.5 mm)
High Voltage Arc Tracking Rate (HVTR)PLC 0
High Voltage, Low Current Arc ResistancePLC 6
THERMAL PROPERTIESVALUETEST METHOD
Relative Thermal Index – Electrical StrengthUL 746B
1.5 mm50   °C
3.0 mm50   °C
Relative Thermal Index – Mechanical ImpactUL 746B
1.5 mm50   °C
3.0 mm50   °C
Relative Thermal Index – Mechanical StrengthUL 746B
1.5 mm50   °C
3.0 mm50   °C

Related Kibisan® SAN (aS) Plastics

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top