Chimei Polylac PA-709 ABS Resin

Polylac® PA-709 Super Impact General ABS Resin

Polylac PA-709 is a high-performance ABS material used in medical and industrial applications. It offers low monomer residue (EU 10/2011) and ISO10993 biocompatibility. With high impact strength (37 kJ/m²) and tensile strength (40 MPa), it is durable even in cold conditions. Easy to mold at 220°C and with UL94 HB flammability standards, it is ideal for medical, electrical, or durable parts.

  • Application: Plumbing fittings/front and rear vehicle spoiler/motorcycle fenders/safety helmets/water filter casings
  • Character: Ultra high impact strength/good low temperature resistance
contact us
Drag & Drop Files, Choose Files to Upload You can upload up to 10 files.
* We prioritize your privacy and ensure information security.
=

Download

Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides.
All documents are sourced directly from manufacturers and updated regularly for accuracy.

ISO TDSDownload
ASTM TDSDownload
MSDSDownload
UL Product iQDownload
RoHSDownload
REACH SVHCDownload
Process GuideDownload
Chimei Polylac® PA-709 Application

Safe for Medical Use

Polylac PA-709 ABS resin meets EU 10/2011 standards for low monomer residue and passes ISO10993 biocompatibility tests. This makes it ideal for medical devices like housings or too

High Strength & Durability

With a tensile strength of 40 MPa and Izod impact resistance of 37 kJ/m² (23°C), PA-709 ABS resists cracks and wear. It stays tough even in cold environments (-30°C), perfect for equipment needing long-lasting performance.

Easy to Process Safely

The resin’s melt flow index of 6 ml/10min (220°C) ensures smooth molding. Pre-dry at 80–85°C for 2–4 hours, and mold below 240°C to avoid degradation. Its UL94 HB flammability rating adds safety for electrical or medical parts.

Chimei Polylac® PA-709

Polylac® PA-709 Datasheet

General ABS POLYLAC® PA-709
Product Description: Super impact
PropertiesISO Test MethodTest ConditionUnitPA-709
Melt Flow Index1133220℃×10KGml/10 min6
Mass Density118323  ℃g/cm31.03
Tensile Strength52750 mm/min, yieldMPa40
50 mm/min, breakMPa31
Tensile Elongation52750 mm/min%35
Flexural Strength1782 mm/minMPa58
Flexural Modulus1782 mm/minGPa1.8
Izod Impact Strength180/1A23℃, NotchedKJ/m237
-30℃, NotchedKJ/m227
Charpy Impact Strength17923℃, NotchedKJ/m238
-30℃, NotchedKJ/m229
Vicat Softening Temp.30650℃/hr;1KG℃105
50℃/hr;5KG℃97
Heat Distortion Temp.75/A1.8MPa, unannealed℃82
1.8MPa, annealed℃98
Coefficient of Linear Thermal Expansion11359––9.3 x 10-5
Flammability–UL-94–1.5mm HB
Mold Shrinkage294-4–%0.4~0.7
Symbol1043––>ABS<
March 11, 2024

Polylac® PA-709 UL Product iQ

POLYLAC® PA-709 UL Product iQ
File Number: E56070Yellow Card™Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets
FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityANSI/UL 94
1.5 mm, Color: ALLHB
3.0 mm, Color: ALLHB
ISO/IEC FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityIEC 60695-11-10
1.5 mm, Color: ALLHB75
3.0 mm, Color: ALLHB40
ELECTRICAL PROPERTIESVALUETEST METHOD
Hot-wire Ignition (HWI)UL 746A
1.5 mmPLC 4
3.0 mmPLC 4
High Amp Arc Ignition (HAI)UL 746A
1.5 mmPLC 0
3.0 mmPLC 0
Comparative Tracking Index (CTI)PLC 1UL 746A
High Voltage Arc Tracking Rate (HVTR)PLC 0
High Voltage, Low Current Arc ResistancePLC 6
THERMAL PROPERTIESVALUETEST METHOD
Relative Thermal Index – Electrical StrengthUL 746B
1.5 mm60   °C
3.0 mm60   °C
Relative Thermal Index – Mechanical ImpactUL 746B
1.5 mm60   °C
3.0 mm60   °C
Relative Thermal Index – Mechanical StrengthUL 746B
1.5 mm60   °C
3.0 mm60   °C
Report Date: 1983-06-23

Related Polylac® ABS Plastics

1 2 3

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top