Chimei Polylac® PA-709S

By /
Chimei Polylac PA-709S ABS Resin

Polylac® PA-709s Super Impact General ABS Resin

Polylac PA-709S is a high-impact ABS resin that boasts excellent strength and durability. It’s ideal for making pipe materials, appliances, and large containers. With good tensile strength and easy processing, Polylac PA-709S ensures reliable performance across various applications.

  • Application: Pipe materials/appliances/large containers
  • Character: Ultra-high impact resistance
contact us
Drag & Drop Files, Choose Files to Upload You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Download

Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides.
All documents are sourced directly from manufacturers and updated regularly for accuracy.

ISO TDSDownload
ASTM TDSDownload
MSDSDownload
UL Product iQDownload
RoHSDownload
REACH SVHCDownload
Process GuideDownload
Chimei Polylac® PA-709S Application

High Impact Resistance

Polylac PA-709S ABS resin boasts ultra-high impact resistance, making it ideal for products that need to endure heavy use and potential damage.

Broad Range of Applications

This versatile material is perfect for making pipe materials, appliances, and large containers, ensuring durability and reliability in various industrial uses.

Reliable Material Properties

With good tensile strength, melt flow index, and excellent impact performance, Polylac PA-709S ABS resin ensures consistent quality and dependable results for manufacturers.

Chimei Polylac® PA-709S

Polylac® PA-709S Datasheet

Extrusion ABS POLYLAC® PA-709S
Product Description: Super impact Extrusion
PropertiesISO Test MethodTest ConditionUnitPA-709S
Melt Flow Index1133220℃×10KGml/10 min4
Mass Density118323  ℃g/cm31.03
Tensile Strength52750 mm/min, yieldMPa37
50 mm/min, breakMPa29
Tensile Elongation52750 mm/min%35
Flexural Strength1782 mm/minMPa51
Flexural Modulus1782 mm/minGPa1.5
Izod Impact Strength180/1A23℃, NotchedKJ/m240
-30℃, NotchedKJ/m228
Charpy Impact Strength17923℃, NotchedKJ/m242
-30℃, NotchedKJ/m230
Vicat Softening Temp.30650℃/hr;1KG℃104
50℃/hr;5KG℃98
Heat Distortion Temp.75/A1.8MPa, unannealed℃81
1.8MPa, annealed℃96
Coefficient of Linear Thermal Expansion11359––9.5 x 10-5
Flammability–UL-94–1.5mm HB
Mold Shrinkage294-4–%0.4~0.7
Symbol1043––>ABS<
March 11, 2024

Polylac® PA-709S UL Product iQ

POLYLAC® PA-709S UL Product iQ
File Number: E56070Yellow Card™Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets
FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityANSI/UL 94
1.5 mm, Color: ALLHB
3.0 mm, Color: ALLHB
ISO/IEC FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityIEC 60695-11-10
1.5 mm, Color: ALLHB75
3.0 mm, Color: ALLHB40
ELECTRICAL PROPERTIESVALUETEST METHOD
Hot-wire Ignition (HWI)UL 746A
1.5 mmPLC 4
3.0 mmPLC 2
High Amp Arc Ignition (HAI)UL 746A
1.5 mmPLC 0
3.0 mmPLC 0
Comparative Tracking Index (CTI)PLC 0UL 746A
High Voltage Arc Tracking Rate (HVTR)PLC 0
High Voltage, Low Current Arc ResistancePLC 7
THERMAL PROPERTIESVALUETEST METHOD
Relative Thermal Index – Electrical StrengthUL 746B
1.5 mm60   °C
3.0 mm60   °C
Relative Thermal Index – Mechanical ImpactUL 746B
1.5 mm60   °C
3.0 mm60   °C
Relative Thermal Index – Mechanical StrengthUL 746B
1.5 mm60   °C
3.0 mm60   °C
Report Date: 1983-06-23

Related Polylac® ABS Plastics

1 2 3

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top