Chimei Polylac® PA-747S A01 Standard White Color

Polylac® PA-747S A01 Standard White Color Pre-colored

Polylac PA-747S A01 is a high-impact, pre-colored white ABS resin engineered for extrusion and injection molding. With superior strength, smooth flow, and thermal stability, it’s ideal for demanding industrial applications requiring durability and consistent aesthetics.

Character: High strength for extrusion, injection, standard white pre-colored

ABS Resin

Chimei POLYLAC® ABS Resin

Key technical data (ISO)

Melt Flow Index: 6 ml/10min (220°C/10KG)
Impact Strength: 35 KJ/m² (23°C, Notched)
Thermal Resistance: Vicat 106°C / HDT 96°C (1.8MPa)
Flammability Rating: UL94 HB (1.5mm)
Mold Shrinkage: 0.4–0.7%

Download

ISO TDS Download

ASTM TDS Download

MSDS Download

Process Guide Download

UL Product iQ Download

Exceptional Impact Resistance

The White ABS POLYLAC® PA-747S A01 delivers 35 KJ/m² Izod impact strength (23°C), ensuring parts like automotive trim or appliance panels resist cracking during assembly or daily use.

Effortless Processing

A Melt Flow Index of 6 ml/10min (220°C/10KG) allows seamless filling of complex molds, reducing cycle times for injection-molded components like housings or protective covers.

Reliable Thermal Performance

With a Vicat softening temperature of 106°C, this Chimei PA-747S A01 ABS maintains structural integrity in high-heat environments, such as near electronics or under UV coatings.

Applications

Sheet Extrusion: Durable panels for appliances, signage, or automotive interiors.
High-Impact Injection Parts: Protective equipment, tool housings, and consumer electronics.
Thermally Stable Components: Parts exposed to heat, such as lighting fixtures or HVAC ducts.

Polylac® PA-747S A01 Datasheet

White ABS POLYLAC® PA-747S_A01 Product Description: High impact, Extrusion,white
Properties	ISO Test Method	Test Condition	Unit	PA-747S_A01
Melt Flow Index	1133	220℃×10KG	ml/10 min	6
Mass Density	1183	23 ℃	g/cm3	1.07
Tensile Strength	527	50 mm/min, yield	MPa	40
Tensile Strength	527	50 mm/min, break	MPa	30
Tensile Elongation	527	50 mm/min	%	35
Flexural Strength	178	2 mm/min	MPa	60
Flexural Modulus	178	2 mm/min	GPa	2
Izod Impact Strength	180/1A	23℃, Notched	KJ/m2	35
Izod Impact Strength	180/1A	-30℃, Notched	KJ/m2	–
Charpy Impact Strength	179	23℃, Notched	KJ/m2	35
Charpy Impact Strength	179	-30℃, Notched	KJ/m2	–
Vicat Softening Temp.	306	50℃/hr;1KG	℃	106
Vicat Softening Temp.	306	50℃/hr;5KG	℃	101
Heat Distortion Temp.	75/A	1.8MPa, unannealed	℃	–
Heat Distortion Temp.	75/A	1.8MPa, annealed	℃	96
Coefficient of Linear Thermal Expansion	11359	–	–	8.6 x 10-5
Flammability	–	UL-94	–	1.5mm HB
Mold Shrinkage	294-4	–	%	0.4~0.7
Symbol	1043	–	–	>ABS<
March 12, 2025 Notes：These are typical properties only and are not to be construed as specifications. Users should confirm results by their own test

Polylac® PA-747S A01 UL Product iQ

POLYLAC® PA-747S A01 \| UL Product iQ
File Number: E56070	Yellow Card™	Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets
FLAMMABILITY PROPERTIES	VALUE	TEST METHOD
Flammability		ANSI/UL 94
1.5 mm, Color: WT	HB
3.0 mm, Color: WT	HB
ISO/IEC FLAMMABILITY PROPERTIES	VALUE	TEST METHOD
Flammability		IEC 60695-11-10
1.5 mm, Color: WT	HB75
3.0 mm, Color: WT	HB40
ELECTRICAL PROPERTIES	VALUE	TEST METHOD
Hot-wire Ignition (HWI)		UL 746A
1.5 mm	PLC 3
3.0 mm	PLC 3
High Amp Arc Ignition (HAI)		UL 746A
1.5 mm	PLC 0
3.0 mm	PLC 0
Comparative Tracking Index (CTI)	PLC 1	UL 746A
High Voltage Arc Tracking Rate (HVTR)	PLC 0
High Voltage, Low Current Arc Resistance	PLC 6
THERMAL PROPERTIES	VALUE	TEST METHOD
Relative Thermal Index – Electrical Strength		UL 746B
1.5 mm	60 °C
3.0 mm	60 °C
Relative Thermal Index – Mechanical Impact		UL 746B
1.5 mm	60 °C
3.0 mm	60 °C
Relative Thermal Index – Mechanical Strength		UL 746B
1.5 mm	60 °C
3.0 mm	60 °C