TAIRIPRO K1035 is a high-performance polypropylene homopolymer resin designed for injection molding. With high fluidity, excellent stiffness, and superior surface luster, this PP K1035 resin streamlines production while delivering durable, visually appealing results for thin-walled parts, housewares, and toys.

Basic Features:

  • Manufacturer: FCFC (Formosa Chemicals & Fibre Corporation）
  • Character: High fluidity, Good Stiffness, Good luster
contact us
Please enable JavaScript in your browser to complete this form.
Click or drag files to this area to upload. You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Key technical data (ISO)

  • Melt Flow Index: 38 g/10 min (ISO 1133)
  • Heat Resistance: 110°C HDT
  • Safety Compliance: UL 94 HB flammability rating
  • Molding Shrinkage: 1.4–1.8%

Download

ISO Data SheetDownload
Safety Data Sheet SDSDownload
UL Product iQDownload
REACH SVHCDownload
Processing DataDownload

Effortless Mold Filling

TAIRIPRO K1035’s 38 g/10 min melt flow index ensures rapid, uniform flow into intricate molds. This reduces cycle times and minimizes defects in thin-walled designs like food containers or toy components.

Reliable Structural Integrity

A flexural modulus of 14,000 MPa provides outstanding rigidity, making it ideal for housewares (e.g., storage bins) or lightweight automotive parts that require dimensional stability under stress.

Premium Surface Finish

With Rockwell hardness R-102 and inherent gloss, TAIRIPRO PP resin creates smooth, scratch-resistant surfaces—perfect for consumer goods like toys or kitchenware that demand aesthetic appeal.

TAIRIPRO K4535 PP resin

Applications

  • Thin-Wall Parts: Food packaging, disposable cups, and medical containers
  • Housewares: Durable storage boxes, kitchen utensils, and appliance components
  • Toys: Intricate action figures, snap-fit components, and outdoor playsets
TAIRIPRO PP resin K4535 Application

Tairipro® K1035 Datasheet

Injection Molding Grade FCFC TAIRIPRO® K1035 Data Sheet
Product Description: High fluidity, Good Stiffness, Good luster
PropertyUnitTest MethodTest ConditionModel K1035
Melt Flow Indexg/10 minISO 1133230℃ × 2.16kg38
IZOD Impact StrengthkJ/m²ISO 18023℃，1/8″，Notched2
IZOD Impact StrengthkJ/m²ISO 18023℃，4mm，Notched2
Specific Gravity–ISO 118323℃/23℃0.9
Tensile StrengthMpaISO 52723℃，50mm/min33
Tensile Elongation at break%ISO 52723℃，50mm/min>50
Flexural ModulusMpaISO 17823℃14000
Rockwell HardnessR-scaleISO 2039-223℃R-102
Heat Deflection Temperature℃ISO 75/AUnannealed，0.455Mpa 1/4″ thickness，120℃/h110
Molding Shrinkage%FCFC Method23℃1.4 ~ 1.8
CombustibilityUL-94File No. E162823HB 1.5 mm
All tests were run under laboratory conditions, ASTM, ISO testing procedures.
The data are intended as a general guide only.
Formosa Chemicals & Fibre Corp. Plastics Div.

Tairipro® K1035 UL Product iQ

TAIRIPRO® K1035 UL Product iQ
File Number: E162823Polypropylene (PP), pellets
FlammabilityValueTest Method
Flame Rating
1.5 mm, ALLHBUL 94
1.5 mm, ALLHB75IEC 60695-11-10, -20
ElectricalValueTest Method
Hot-wire Ignition (HWI) (1.5 mm)PLC 3UL 746
High Amp Arc Ignition (HAI) (1.5 mm)PLC 3UL 746
Comparative Tracking Index (CTI)PLC 0UL 746
High Voltage Arc Tracking Rate (HVTR)PLC 0UL 746
Arc ResistancePLC 4ASTM D495
ThermalValueTest Method
RTI ElecUL 746
1.5 mm65.0°C
3.0 mm65.0°C
RTI ImpUL 746
1.5 mm65.0°C
3.0 mm65.0°C
RTI StrUL 746
1.5 mm65.0°C
3.0 mm65.0°C

Related Tairipro® PP Plastics

1 2 3

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top