Chimei Polylac® PA-709P ABS Extrusion Grade

Polylac® PA-709P ABS Extrusion grade Pipe material

Chimei POLYLAC PA-709P is an extrusion-grade ABS resin designed for high-efficiency pipe production. With superior melt flow, impact resistance, and heat stability, it’s ideal for industrial, plumbing, and HVAC systems—delivering durability and safety compliance.

Character: Dedicated extruder pipes

ABS Resin

Chimei POLYLAC® ABS Resin

Key technical data (ISO)

Melt Flow Rate: 5 ml/10min (220°C, 10kg)
Tensile Strength: 42 MPa
Impact Strength (Izod): 39 kJ/m² (23°C)
Heat Resistance: Vicat 106°C / HDT 98°C
Flammability: HB-rated (1.5mm)
Density: 1.04 g/cm³

Download

ISO TDS Download

ASTM TDS Download

MSDS Download

Process Guide Download

UL Product iQ Download

Optimized Melt Flow for Efficiency

POLYLAC PA-709P’s melt flow index (5 ml/10min) ensures smooth extrusion, reducing energy use and speeding up production for cost-effective pipe manufacturing.

Exceptional Impact Resistance

Boasting 39 KJ/m² Izod impact strength, this ABS resin withstands drops, collisions, and harsh environments, perfect for industrial drainage or heavy-duty piping.

Heat Resistance & Safety Compliance

With a Vicat softening point of 106°C and HB flammability rating, it ensures safe performance in high-temperature applications like hot water pipes or HVAC ducting.

Applications

Industrial Drainage Pipes
Plumbing Systems
HVAC Ducting
Fire-Safe Building Materials

Polylac® PA-709p Datasheet

Extrusion ABS POLYLAC® PA-709P Product Description: Dedicated extruder pipes
Properties	ISO Test Method	Test Condition	Unit	PA-709P
Melt Flow Index	1133	220℃×10KG	ml/10 min	5
Mass Density	1183	23 ℃	g/cm3	1.04
Tensile Strength	527	50 mm/min, yield	MPa	42
Tensile Strength	527	50 mm/min, break	MPa	31
Tensile Elongation	527	50 mm/min	%	25
Flexural Strength	178	2 mm/min	MPa	61
Flexural Modulus	178	2 mm/min	GPa	2
Izod Impact Strength	180/1A	23℃, Notched	KJ/m2	39
Izod Impact Strength	180/1A	-30℃, Notched	KJ/m2	–
Charpy Impact Strength	179	23℃, Notched	KJ/m2	39
Charpy Impact Strength	179	-30℃, Notched	KJ/m2	–
Vicat Softening Temp.	306	50℃/hr;1KG	℃	106
Vicat Softening Temp.	306	50℃/hr;5KG	℃	99
Heat Distortion Temp.	75/A	1.8MPa, unannealed	℃	–
Heat Distortion Temp.	75/A	1.8MPa, annealed	℃	98
Coefficient of Linear Thermal Expansion	11359	–	–	8.7 x 10-5
Flammability	–	UL-94	–	1.5mm HB
Mold Shrinkage	294-4	–	%	0.4~0.7
Symbol	1043	–	–	>ABS<
March 12, 2025 Notes：These are typical properties only and are not to be construed as specifications. Users should confirm results by their own test

Polylac® PA-709p UL Product iQ

POLYLAC® PA-709P \| UL Product iQ
File Number: E56070	Yellow Card™	Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets
FLAMMABILITY PROPERTIES	VALUE	TEST METHOD
Flammability		ANSI/UL 94
1.5 mm, Color: ALL	HB
3.0 mm, Color: ALL	HB
ISO/IEC FLAMMABILITY PROPERTIES	VALUE	TEST METHOD
Flammability		IEC 60695-11-10
1.5 mm, Color: ALL	HB75
3.0 mm, Color: ALL	HB40
ELECTRICAL PROPERTIES	VALUE	TEST METHOD
Hot-wire Ignition (HWI)		UL 746A
1.5 mm	PLC 3
3.0 mm	PLC 3
High Amp Arc Ignition (HAI)		UL 746A
1.5 mm	PLC 0
3.0 mm	PLC 0
Comparative Tracking Index (CTI)	PLC 0	UL 746A
High Voltage Arc Tracking Rate (HVTR)	PLC 1
High Voltage, Low Current Arc Resistance	PLC 6
THERMAL PROPERTIES	VALUE	TEST METHOD
Relative Thermal Index – Electrical Strength		UL 746B
1.5 mm	60 °C
3.0 mm	60 °C
Relative Thermal Index – Mechanical Impact		UL 746B
1.5 mm	60 °C
3.0 mm	60 °C
Relative Thermal Index – Mechanical Strength		UL 746B
1.5 mm	60 °C
3.0 mm	60 °C