Chimei Polylac® PA-757 A01 ABS

By /
Chimei POLYLAC PA-757 A01 ABS Plastic

Polylac® PA-757 A01 Standard White Color Pre-colored


POLYLAC PA-757 A01, Chimei’s premier White ABS resin, known for its high gloss and medium impact strength. This versatile material is perfect for creating durable and visually appealing products. With excellent mechanical strength, thermal stability, and flame retardancy, it meets the demands of modern manufacturing, offering both performance and aesthetic flexibility.

  • Character: High rigidity, medium impact strength, standard-white and pre-colored
  • Application: Household Appliances; Cosmetics Containers
contact us
Drag & Drop Files, Choose Files to Upload You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Key technical data (ISO)

  • Density: 1.07 g/cm³
  • Tensile Strength (Yield): 47 MPa
  • Flexural Modulus: 2.4 GPa
  • Izod Impact Strength (Notched, 23°C): 17 KJ/m²
  • Heat Distortion Temperature (Annealed) : 98°C
  • Flammability HB: (UL-94)
  • Mold Shrinkage: 0.4~0.7%

Download

ISO TDSDownload
ASTM TDSDownload
MSDSDownload
Process GuideDownload
UL Product iQDownload

Unmatched Rigidity

With a flexural modulus of 2.4 GPa, Chimei ABS Resin PA757 A01 ensures your products maintain their shape and structural integrity, even under significant stress. Ideal for load-bearing components in appliances and equipment, this feature reduces the risk of deformation, saving you time and costs on replacements.

Dependable Impact Resistance

Boasting an Izod impact strength of 17 KJ/m², this White ABS POLYLAC® PA-757 A01 can withstand moderate impacts, making it suitable for products that might be dropped or knocked around, like office printers or cosmetic jars. This durability ensures your products stand up to daily wear and tear, enhancing customer satisfaction.

Striking Aesthetic Finish

The high-gloss surface of POLYLAC PA-757 A01 enhances the visual appeal of your products, while its availability in standard-white and various pre-colored options allows for easy customization to match your brand’s aesthetic. This eliminates the need for secondary finishing processes, streamlining your production workflow.

Chimei POLYLAC PA-757 A01 ABS

Applications

  • Household Appliances: refrigerators and washing machines
  • Cosmetics Containers
  • Office Appliances: printers and copiers
Chimei POLYLAC PA-757 A01 application

Polylac® PA-757 A01 Datasheet

White ABS POLYLAC®  PA-757_A01
Product Description: High gloss, Medium impact,white
PropertiesISO Test MethodTest ConditionUnitPA-757_A01
Melt Flow Index1133 220℃×10KGml/10 min18 
Mass Density1183 23 ℃g/cm31.07 
Tensile Strength527 50 mm/min, yieldMPa47 
50 mm/min, breakMPa35 
Tensile Elongation527 50 mm/min%40 
Flexural Strength178 2 mm/minMPa70 
Flexural Modulus2 mm/minGPa2.4 
Izod Impact Strength180/1A23℃, NotchedKJ/m217 
-30℃, NotchedKJ/m2–
Charpy Impact Strength179 23℃, NotchedKJ/m217 
-30℃, NotchedKJ/m2–
Vicat Softening Temp.306 50℃/hr;1KG℃106 
50℃/hr;5KG℃99 
Heat Distortion Temp.75/A1.8MPa, unannealed℃–
1.8MPa, annealed℃98 
Coefficient of Linear Thermal Expansion11359 ––7.9 x 10-6
Flammability–UL-94–1.5mm HB
Mold Shrinkage294-4–%0.4~0.7
Symbol1043 ––>ABS<
March  12, 2025
Notes：These are typical properties only and are not to be construed as specifications. Users should confirm results by their own test

Polylac® PA-757 A01 UL Product iQ

POLYLAC® PA-757 A01 | UL Product iQ
File Number: E56070Yellow Card™Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets
FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityANSI/UL 94
1.5 mm, Color: WTHB
3.0 mm, Color: WTHB
ISO/IEC FLAMMABILITY PROPERTIESVALUETEST METHOD
FlammabilityIEC 60695-11-10
1.5 mm, Color: WTHB75
3.0 mm, Color: WTHB40
ELECTRICAL PROPERTIESVALUETEST METHOD
Hot-wire Ignition (HWI)UL 746A
1.5 mmPLC 4
3.0 mmPLC 3
High Amp Arc Ignition (HAI)UL 746A
1.5 mmPLC 0
3.0 mmPLC 0
Comparative Tracking Index (CTI)PLC 0UL 746A
High Voltage Arc Tracking Rate (HVTR)PLC 1
High Voltage, Low Current Arc ResistancePLC 7
THERMAL PROPERTIESVALUETEST METHOD
Relative Thermal Index – Electrical StrengthUL 746B
1.5 mm85   °C
3.0 mm85   °C
Relative Thermal Index – Mechanical ImpactUL 746B
1.5 mm80   °C
3.0 mm80   °C
Relative Thermal Index – Mechanical StrengthUL 746B
1.5 mm85   °C
3.0 mm85   °C

Related Polylac® ABS Plastics

1 2 3

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top