FCFC Formosa TAIRIPRO® K8095

By /
FCFC TAIRIPRO PP resin Impact Copolymer

TAIRIPRO® K8095 Impact Copolymer Injection Molding

TAIRIPRO® K8095 is an impact copolymer polypropylene (PP) resin. With high fluidity, excellent impact strength (even at low temperatures), high stiffness, and low warpage, this material is ideal for injection-molded components requiring precision, structural integrity, and resistance to mechanical stress. Its balanced properties make it a versatile choice for industrial and consumer goods.

  • Character: High fluidity, Good impact strength, Good Stiffness
  • Application: Automotive parts
contact us
Please enable JavaScript in your browser to complete this form.
Click or drag files to this area to upload. You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Key technical data (ISO)

  • Melt Flow Rate: 95 g/10min (ISO 1133, 230°C/2.16kg)
  • Impact Strength: 69 kJ/m² at 23°C (ISO 180, 1/8″ notch), 44 kJ/m² at -18°C (ISO 180, 4mm notch)
  • Heat Resistance: 108°C HDT (ISO 75/A, 0.455MPa)
  • Tensile Strength: 21 MPa (ISO 527)
  • Flexural Modulus: 980 MPa (ISO 178)
  • Certifications: FDA 21 CFR 177.1520 compliant, RoHS

Download

ISO Data SheetDownload
ASTM Data SheetDownload
Safety Data Sheet SDSDownload
Processing DataDownload

Features & Benefits

Rapid Mold Filling & Efficiency

The high melt flow rate (95 g/10min) enables fast injection molding cycles, reducing production time by up to 20% compared to standard PP resins. This translates to lower energy costs and higher throughput for automotive part manufacturers.

Toughness Across Temperatures

With IZOD impact strength of 7 kg·cm/cm at 23°C and 4.5 kg·cm/cm at -20°C, this resin withstands harsh environments, making it perfect for exterior automotive components like bumpers or under-hood parts that face thermal and mechanical stress.

Dimensional Stability & Precision

A low molding shrinkage rate (1.4–1.8%) and high flexural modulus (10,000 kg/cm²) ensure tight tolerances and minimal warping, critical for intricate parts such as interior trim panels or structural housings.

FCFC Formosa TAIRIPRO PP Impact Copolymer

Application

Interior Components

Dashboard panels, door handles, and trim with high surface finish requirements.

Structural Parts

Bumper supports, battery housings, and underbody shields demanding impact resistance.

Thermal Management

Engine covers and cooling system parts stable up to 108°C.

High-Precision Molds

Thin-walled connectors and clips requiring minimal shrinkage.

Tairipro K8095 PP Resin application

Related Tairipro® PP Plastics

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top