FCFC TAIRIPRO PP resin Impact Copolymer

TAIRIPRO® K8802 Impact Copolymer Injection Molding

TAIRIPRO® K8802 is a high-performance polypropylene (PP) impact copolymer resin engineered for demanding industrial applications. With exceptional impact strength, resistance to low-temperature brittleness, and a glossy finish, it excels in injection-molded products requiring durability and aesthetics. Ideal for suitcase components.

  • Character: Hight impact strength,Excellent resistance to low temp. Brittleness, Good luster
  • Application: Suitcase Parts
contact us
Please enable JavaScript in your browser to complete this form.
Click or drag files to this area to upload. You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Key technical data (ISO)

  • Melt Flow Index: 2 g/10 min (230°C, 2.16kg | ISO 1133)
  • Tensile Strength: 270 kg/cm² (ASTM D-638) / 26.5 MPa (ISO 527)
  • Flexural Modulus: 11,000 kg/cm² (ASTM D-790) / 1,078 MPa (ISO 178)
  • Molding Shrinkage: 1.5–1.9% (23°C | FCFC Method)
  • Heat Deflection Temperature: 105°C (0.45MPa | ASTM D-648)
  • Flammability Rating: HB (UL 94)

Download

ISO Data SheetDownload
ASTM Data SheetDownload
Safety Data Sheet SDSDownload
Processing DataDownload
UL Product iQDownload

Features & Benefits

Exceptional Impact Resistance

TAIRIPRO K8802 delivers 70 kg·cm/cm notched IZOD impact strength at 23°C (ASTM D-256), minimizing breakage in high-stress scenarios like luggage handling. This ensures longer product life and reduced returns for manufacturers.

Reliable Low-Temperature Performance

With 10 kg·cm/cm impact resistance at -20°C, this resin retains toughness in cold environments, preventing cracks in components like winter travel gear or automotive parts exposed to harsh climates.

Premium Surface Finish

The material’s inherent high-gloss luster eliminates the need for post-processing painting or coatings, saving time and costs while enhancing visual appeal for consumer-facing products like suitcase shells.

FCFC Formosa TAIRIPRO PP Impact Copolymer

Application

Shells & Frames

High impact resistance withstands rough handling during travel.

Handle Components

It retains structural integrity under repetitive stress.

Latches & Zippers

It resists brittleness in sub-zero cargo holds.

Tairipro K8802 PP Resin application

Related TAIRIPRO® PP Plastics

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top