FCFC TAIRIPRO® S1019 Multi-Filament Grade

TAIRIPRO® S1019 Homopolymer PP Multi-Filament Grade

FCFC’s TAIRIPRO S1019 is a controlled-rheology polypropylene resin engineered for superior processability, exceptional softness, and anti-gas fading. Perfect for high-speed fiber production, it delivers consistent melt flow (MFI 19 g/10min) and excellent mechanical stability.

Character: Controlled rheology, Good softness, Anti gas fading
Application: Staple fiber, ES fiber & PP staple fiber

Polypropylene PP Resin

FCFC TAIRIPRO® PP resin

Key technical data (ISO)

Melt Flow Index (230°C): 19 g/10 min (ISO 1133)
Tensile Strength: 33 MPa (ISO 527)
Elongation at Break: >200% (ISO 527)
Flexural Modulus: 1,372 MPa (ISO 178)
Notched Impact Strength: 27 kJ/m² (23°C) (ISO 180)
Heat Deflection Temp: 110°C (0.455 MPa) (ISO 75/A)

Download

Tairipro S1019 ISO Data Sheet Download

Tairipro S1019 ASTM Data Sheet Download

Tairipro S1019 Processing Data pp Download

Features & Benefits

Precision Melt Flow Control

With an optimal MFI of 19 g/10min (ISO 1133), S1019 ensures smooth extrusion and minimal downtime. Ideal for high-volume fiber lines needing reliable throughput.

Enhanced Fiber Softness

Specific gravity of 0.9 and >200% elongation (ISO 527) create lightweight, flexible fibers. Elevate comfort in textiles without compromising durability.

Fade-Resistant Performance

Anti-gas fading properties maintain color integrity in dyed fibers. Critical for vibrant, long-lasting textiles exposed to UV or chemical environments.

Application

Staple Fiber

Consistent spinning for nonwovens, geotextiles, and hygiene products.

ES Fiber

Uniform bonding in thermal-bonded nonwovens (e.g., medical masks, wipes).

PP Staple Fiber

High-strength yarns for ropes, carpets, and agrotextiles.