FCFC TAIRIPRO® T1002 Extrusion Grade

TAIRIPRO® T1002 Homopolymer PP Extrusion Grade

Tairipro T1002 is a premium homopolymer polypropylene resin engineered for extrusion and blow molding. With excellent tensile strength, this versatile Tairipro T1002 pp resin ensures durability and reliability in demanding industrial applications. Ideal for high-stress components, it balances processability and performance seamlessly.

Character: Excellent tensile strength
Application: Corrugated sheet, Strapping, Bottles

Polypropylene PP Resin

FCFC TAIRIPRO® PP resin

Key technical data (ISO)

Melt Flow Index: 1.7 g/10 min (230°C, 2.16 kg)
Tensile Strength: 35 MPa | Elongation at Break: >200%
Impact Strength: 49 kJ/m² (notched, 23°C)
Flexural Modulus: 1,470 MPa
Heat Resistance: 110°C (HDT @ 0.455 MPa)
Molding Shrinkage: 1.5–1.9%
Flammability: UL 94 HB (1.5–1.65 mm)
Specific Gravity: 0.9

Download

Tairipro T1002 ISO Data Sheet Download

Tairipro T1002 ASTM Data Sheet Download

Tairipro T1002 Processing Data pp Download

Tairipro T1002 UL Product iQ Download

Features & Benefits

Superior Tensile Strength

Tairipro T1002 delivers 35 MPa tensile strength (ISO 527), resisting deformation under heavy loads. This means longer-lasting products like industrial strapping or crates.

Easy Processing Flexibility

With a melt flow index of 1.7 g/10 min (ISO 1133), Tairipro T1002 pp resin flows smoothly during extrusion/blow molding. Reduces energy use and shortens cycle times.

Safety-Compliant Performance

Rated UL 94 HB (1.5–1.65 mm), this Tairipro pp resin minimizes fire risks. Non-hazardous (per SDS) and thermally stable up to 110°C.

Application

Corrugated Sheets

Roofing/partition panels with weather resistance.

Strapping

High-tension packaging bands for logistics.

Bottles

Chemical-resistant containers for detergents or industrial fluids.